You are currently viewing our boards as a guest, which gives you limited access to view most discussions and access our other features. By joining our free community, you will have access to post topics, communicate privately with other members (PM), respond to polls, upload content, and access many other special features. In addition, registered members also see less advertisements. Registration is fast, simple, and absolutely free, so please, join our community today!





 Page 2 of 3 [ 21 posts ]  Go to page Previous  1, 2, 3  Next
Author Message
 Post subject: Re: Laser 120 Petty or Kohetsu 120 petty
PostPosted: Thu Jan 23, 2014 10:16 pm 

Joined: Mon May 14, 2012 5:03 pm
Posts: 45
Location: Austin, TX
at least with the shimo & yuki series..



_________________
Don't talk about it, be about it!
Offline
 Profile  
 
 Post subject: Re: Laser 120 Petty or Kohetsu 120 petty
PostPosted: Thu Jan 23, 2014 10:36 pm 

Joined: Wed Jan 15, 2014 3:40 pm
Posts: 271
I have a mizu suji, and pretty happy with thinness behind edge on that one, might take a look there too as It is blue #2 where the yuki and shimo are w#2. NOT stainless clad but the kurouchi does add almost the same effect as a stainless clad. almost same height a little heavier but just pointing out another option. what ever one you pick im sure youll be happy. all great lines.


Offline
 Profile  
 
 Post subject: Re: Laser 120 Petty or Kohetsu 120 petty
PostPosted: Thu Jan 23, 2014 10:43 pm 
User avatar

Joined: Wed Nov 21, 2012 10:17 pm
Posts: 7621
Location: Derby City, Kentucky
White steel will sharpen easier and take a slightly better edge. AS steel will hold it's edge longer than white steel. These differences are very slight and only those with the most keen of touch could tell a difference.



_________________
If God wanted me to be a vegetarian he wouldn't have made animals taste so good.
Offline
 Profile  
 
 Post subject: Re: Laser 120 Petty or Kohetsu 120 petty
PostPosted: Thu Jan 23, 2014 10:52 pm 

Joined: Mon May 14, 2012 5:03 pm
Posts: 45
Location: Austin, TX
is one more reactive than the other?



_________________
Don't talk about it, be about it!
Offline
 Profile  
 
 Post subject: Re: Laser 120 Petty or Kohetsu 120 petty
PostPosted: Thu Jan 23, 2014 10:55 pm 
User avatar

Joined: Wed Nov 21, 2012 10:17 pm
Posts: 7621
Location: Derby City, Kentucky
There are no absolutes when it comes to reactivity other than carbon is.



_________________
If God wanted me to be a vegetarian he wouldn't have made animals taste so good.
Offline
 Profile  
 
 Post subject: Re: Laser 120 Petty or Kohetsu 120 petty
PostPosted: Thu Jan 23, 2014 11:13 pm 

Joined: Thu May 24, 2012 12:20 am
Posts: 4127
Jeff speaks truth.

Most users would be hard pressed to tell Wt from AS steel on the stones, in cutting performance, or in reactivity. Grind, heat treat, and other measures of craftsmanship become more important here. I do not have personal experience with either the Masakage line or the Richmond Laser AS line, but I cannot imagine you would go wrong with either one.

Honestly, if it were me, I would likely go with what is in stock today :D


Offline
 Profile  
 
 Post subject: Re: Laser 120 Petty or Kohetsu 120 petty
PostPosted: Fri Jan 24, 2014 8:14 am 
Forum Moderator

Joined: Tue Feb 05, 2013 12:00 pm
Posts: 4578
Joseph - get the Yuki. You will not be dissapointed :-). If you are going to cut citrus and the like frequently w/your petty, IMO SS clad carbon over a fully reactive blade is desirable. The Yuki will put a smile on your face every time you use it ;-).


Offline
 Profile  
 
 Post subject: Re: Laser 120 Petty or Kohetsu 120 petty
PostPosted: Fri Jan 24, 2014 8:31 am 

Joined: Mon Dec 09, 2013 3:10 pm
Posts: 245
My mistake on the cladding. sorry guys.


Offline
 Profile  
 
 Post subject: Re: Laser 120 Petty or Kohetsu 120 petty
PostPosted: Fri Jan 24, 2014 8:35 am 
Forum Moderator

Joined: Tue Feb 05, 2013 12:00 pm
Posts: 4578
Hey, no big deal. I actually used to mistakenly label the Shimo as mono steel. Doh!


Offline
 Profile  
 
 Post subject: Re: Laser 120 Petty or Kohetsu 120 petty
PostPosted: Fri Jan 24, 2014 8:48 am 
Forum Moderator
User avatar

Joined: Mon Apr 23, 2012 1:36 pm
Posts: 3330
I have found AS to be slightly less reactive than white steel. But not so much I'd buy based on that.



_________________
Adam

Image
http://marrknives.com
http://facebook.com/marrknives
Offline
 Profile  
 
Display posts from previous:  Sort by  
 Page 2 of 3 [ 21 posts ]  Go to page Previous  1, 2, 3  Next

All times are UTC - 6 hours


Who is online

Users browsing this forum: No registered users and 5 guests


You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot post attachments in this forum

Search for:
Jump to:  


suspicion-preferred